2B 6000mm Length JIS Inconel 600 Tubing Non Magnetic Thermal Stable

Inconel 600 is a nickel-chromium alloy used for applications that require corrosion and high temperature resistance. This nickel alloy was designed for service temperatures from cryogenic to elevated temperatures in the range of 2000° F. It is non-magnetic, has excellent mechanical properties, and presents the desirable combination of high strength and good weldability under a wide range of temperatures. The high nickel content in Inconel 600 enables it to retain considerable resistance under reducing conditions, makes it resistant to corrosion by a number of organic and inorganic compounds, gives it excellent resistance to chloride-ion stress-corrosion cracking and also provides excellent resistance to alkaline solutions. Typical applications of this nickel alloy include the chemical, pulp and paper, aerospace, nuclear engineering and heat treating industries.

• Sheet
• Plate
• Bar
• Pipe & Tube (welded & seamless)
• Fittings (i.e. flanges, slip-ons, blinds, weld-necks, lapjoints, long welding necks, socket welds, elbows, tees, stub-ends, returns, caps, crosses, reducers, and pipe nipples)
• Wire

characteristics

• Resistant to a wide range of corrosive media.
• Virtually immune to chlorine ion stress corrosion cracking
• Non-magnetic
• Excellent mechanical properties
• High strength and good weldability under a wide range of temperatures

Chemical Composition, %

applications

• Chemical industry
• Aerospace
• Heat treating industry
• Pulp and paper industry
• Food processing
• Nuclear Engineering
• Gas turbine components

Fabrication with Inconel 600

Alloy 600 can be both hot formed and cold formed using typical processes. Hot working should be performed between 1600° F and 2250° F avoiding any work between1200-1600° F because the ductility decreases in this temperature range. Welding Alloy 600 can be achieved via shielded metal-arc welding, TIG, and MIG.

ASTM Specifications

Mechanical Properties

Typical room temperature Tensile Properties of Annealed Material